The composite membrane is synthesized using chitosan as a matrix membrane with montmorillonite (MMT) as a filler and modified using polyvinyl alcohol (PVA). The main aim of this study is to find out the influence of PVA concentration and the working temperature toward the permeability of chitosan-MMT/PVA composite membrane. Fourier transform infrared spectroscopy (FTIR) characterization is performed in order to identify the interaction between the chitosan matrix and the modified MMT with PVA. The presence of new absorption at 1116.82 and 619.17 cm-1 indicated the interaction between MMT and PVA. Further, the widening of OH absorption indicated the hydrogen bond which is formed between chitosan matrix and PVA. This interaction is also demonstrated by the evenly distributed surface on scanning electron microscope (SEM) topography analysis. The thermal stability of composite membrane is determined by thermal gravimetry analysis (TGA). In addition, the composite membrane containing PVA has four patterns decomposed. When the TVA is absent from the composite membrane, it has three decomposition patterns, which are shown by TGA analysis. Based on its tensile strength, the composite membrane has good mechanical properties. The proton conductivity of the composite membranes are directly proportional to the PVA concentration. On the other hand, the methanol permeability of composite membranes is inversely proportional with the PVA concentration. The highest proton conductivity was obtained with the addition of 2 % PVA of 2.94×10-4 S cm-1. Further, it also has the lowest methanol permeability with the value of 5.05×10-6 cm2 s-1. As a result, the crosslinked composite membrane chitosan-MMT prepared by PVA-crosslinking technique has the potential to be exploited for the direct methanol fuel cell application. © 2024 Serbian Chemical Society. All rights reserved.
Department of Chemical Engineering, Politeknik Negeri Malang, East Java, Malang, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock